Analysis of the best adhesion strength of UV ink U

  • Detail

The packaging and printing industry is developing rapidly in the direction of fast, multi-color and one-time printing. UV ink and UV varnish have become the new favorites of packaging and printing materials. However, with the time of application and the increasing application fields, people have put forward newer and higher requirements for the above products: they should not dry on the printing machine, but also dry quickly after printing; We should not only have low material costs, but also have high gloss. The action plan for accelerating the development of new material industry in Zhejiang Province (2019 – 2022) is high; It should not only have a long storage period, but also have good adhesion fastness after printing and roller coating

at present, few can meet the above requirements at the same time. Packaging and printing operators are concerned about the adhesion fastness of printing ink film and roll coating film, followed by the ability to flow without caking at low temperature

whether it's UV ink or UV varnish, packaging and printing plants are afraid of operating in high temperature and humidity seasons; The second is afraid that the moisture content of the substrate exceeds the standard. Because it is very easy to pull off the ink film or adhesive film when it is first bolted (adhesive tape paper) after printing or polishing on the above workshop environment and substrate, and it will be returned by users. For example, the author found in Henan Luohe "Shuanghui" group that the ham sausage carton packaging of the group was sealed with adhesive tape. When the adhesive tape was torn off during consumption, the decoration (ink and varnish) on the packaging seal was pulled off in pieces, which reduced the apparent quality of the packaged goods and directly damaged the brand image of the enterprise. Another example is that Nanjing gold foil group undertakes to print the mouthprint on Wuhan Jinlong cigarettes. When the high-speed automatic labeling is at 140 ℃ -160 ℃, it is often difficult to label in the continuous labeling process, or it is not resistant to high temperature, or the printed image and text color blocks fall off during slitting. This not only affects the reputation of the gold foil group with a certain popularity, but also increases the scrap rate for users

based on the analysis of different brands, technical parameters and actual proportions from photo solid resin or prepolymer to crosslinker dosage, from photosensitizer to polymerization inhibitor, it is considered that some existing manufacturers ignore the role of crosslinker. An ideal crosslinker is also an ideal active diluent, which is not only miscible with wax, but also can dissolve and dilute unsaturated polyester and resin, reduce the viscosity of ink and varnish system, and improve ink Liquidity of varnish. And can participate in the UV curing reaction, so it is often less in its formula, resulting in poor ink fluidity and the agglomeration and non frost resistance of varnish; The second is that too much photosensitizer not only can not improve the curing speed, but also the production cost increases correspondingly. Excessive photosensitizer will reduce the conjunctival strength of UV gondola or UV varnish, etc. The preparation of new materials, adjustment of production process, trial use and comparison of application methods, light intensity and light energy records of photochemical reaction process, curing speed and control of workshop ambient temperature and humidity, Pu value of substrate and different moisture content (1%, 2%, 3%, 5%, 6%, 7%, 8%) were carried out on site. After comparison, it was found that the moisture content of paperboard of substrate should be controlled at 3% due to the adhesive of alcohol sol or PVC substrate, Therefore, printing UV ink and roller UV varnish are not easy to flow in the past few years. Poor mobility and poor adhesion of caking are related to water content. To improve the adhesion strength of ink film, one is to replace the new UV ink and UV glazing oil, and the other is to add 3%-6% js-pph (302) film-forming additive from Shanghai Jinshan Chemical Plant, 0.2%-0.5% js-f4011 adhesion promoter or 5%-15% CH3COOC2H5 to the ink or glazing oil, which can ensure the fundamental improvement of the adhesion strength of ink film and glazing oil adhesive film of packaging and printing

this article is from the network, and the copyright belongs to the original author. It is only for everyone to share and learn. If the author believes that infringement is involved, please contact us after signal collection and regression and fitting analysis. We will delete it immediately after verification

Copyright © 2011 JIN SHI